Method for manufacturing semiconductor device and storage medium

ABSTRACT

[Object] It is an object of the present invention to provide a semiconductor device manufacturing method capable of forming a high perpendicularity mask pattern, which is laminated on an etching target film on a substrate, through a resist pattern formed from a resist film laminated on the organic film, for use as an etching mask for the etching target film. 
     [Means for Solving the Problem] There is provided a step of etching an organic film in a multi-layered resist laminated on an etching target film on a substrate, the multi-layered resist including the organic film and a resist film having a resist pattern laminated on the organic film, by a plasma, which has been obtained by making a process gas containing carbon dioxide and hydrogen, along the resist pattern, so as to form a mask pattern for etching the etching target film.

FIELD OF THE INVENTION

The present invention relates to a technique to etch an organic film, which constitutes part of a multi-layered resist, into a mask pattern through which the objective film is etched.

BACKGROUND ART

In the manufacture of semiconductor devices, metal interconnects formed in inter-layer insulation films made of, for example, oxide silicon (SiO₂) are becoming finer and finer. To cope with this trend toward finer interconnects, a three-layer resist is formed in some cases. The three layers are, for example, an organic film, a SiO₂ film by the SOG (Spin On Glass) method, and a photoresist film which are formed in this order on the insulation film.

Specifically, interconnects are formed by using this three-layer resist as described here. After the photoresist film is formed into a resist pattern by photolithography, the SiO₂ film is etched through this resist pattern to form a mask pattern having side walls inclined so that the apertures narrow with depth. Then, after the lower organic film is etched according to the mask pattern to form the organic film into a mask pattern, the insulation film is etched according to the patterns formed from the respective layers. Consequently, recesses are formed as contact holes and via holes where fine interconnect lines, narrower than those of the resist pattern, will be buried. Conventionally, O₂ gas in the plasma state is used to etch the organic film.

In order to further improve semiconductor devices in operation speed, it is demanded to lower the relative dielectric constants of interlayer insulation films. Instead of conventionally used SiO₂, a lower dielectric constant porous film which contains silicon, carbon, oxygen, and hydrogen (SiCOH film) is sometimes used as an interlayer insulation film. However, this SiCOH film is liable to be damaged if exposed to oxygen plasma. In addition, if plasma O₂ gas is used to etch the organic film, the organic film is etched isotropically. In other words, since etching by generated oxygen (O) radicals is active not only downward but also laterally, the organic film has such a bowing profile that each sidewall of the pattern, when viewed in vertical section, is laterally widened like a bow, resulting in a mask pattern with poor perpendicularity sidewalls. If the mask pattern has such a bowing profile, it may be impossible to form sufficiently narrow interconnect lines in the insulation film since the insulation film is etched wider.

Accordingly, the present inventors made an accumulative study of the etching gas and contrived the use of CO₂ gas plasma to etch the organic film. Use of CO₂ gas plasma is effective since it can not only suppress damage to the SiCOH film but also reduce the generation of oxygen radicals as compared with O₂ gas plasma and consequently suppress isotropic etching of the organic film. Since the mask pattern formed from the organic film does not have a considerable bowing profile, it is possible to accurately control the etching width when the organic film and the lower insulation film is etched. With the progress of interconnects in minuteness, however, etching of the organic film is demanded to meet still higher perpendicularity requirements. In the use of CO₂ gas plasma it is becoming difficult to suppress the occurrence of bowing profile sufficiently enough to meet this demand.

Etching of low dielectric constant films by use of a gas composed of H₂ and CO₂ is disclosed in Patent Document 1. Unlike the present invention, however, there is no mention of etching an organic film of a multi-layered resist in forming a mask.

[Patent Document 1] JP-A-2002-16050

DISCLOSURE OF THE INVENTION Problem to be Solved by the Invention

The present invention was made in order to solve the above-mentioned problem. It is an object of the present invention to provide a semiconductor device manufacturing method capable of forming a high perpendicularity mask pattern, which is laminated on an etching target film on a substrate, through a resist pattern formed from a resist film laminated on the organic film, for use as an etching mask for the etching target film. It is another object of the present invention to provide a storage medium having the semiconductor device manufacturing method stored therein.

Means for Solving the Problem

A semiconductor device manufacturing method according to the present invention comprises a step of etching an organic film in a multi-layered resist laminated on an etching target film on a substrate, the multi-layered resist including the organic film and a resist film having a resist pattern laminated on the organic film, by a plasma, which has been obtained by making a process gas containing carbon dioxide and hydrogen, along the resist pattern, so as to form a mask pattern for etching the etching target film.

The organic film is embedded in a low dielectric constant film formed on the substrate, the low dielectric constant film containing silicon, carbon, oxygen, and hydrogen. In this case, the organic film is a sacrificial film. In addition, the recess of the low dielectric constant film may become a via hole where an electrode is buried to connect an upper interconnect layer and a lower interconnect layer in a multi-layered interconnection structure. The organic film contains carbon as a main component, for example.

A storage medium according to the present invention is a storage medium storing a computer program executable by a computer, the program being used in a plasma processing apparatus for etching a substrate, wherein the computer program incorporates steps for performing the aforementioned semiconductor manufacturing method.

EFFECT OF THE INVENTION

According to the present invention, as apparent from experimental results mentioned later, it is possible to form an organic film, which constitutes apart of a multi-layered resist, into a high perpendicularity mask pattern by etching the organic film with plasma which is created by exciting a process gas containing carbon dioxide and hydrogen.

BEST MODE FOR CARRYING OUT THE INVENTION

With reference to FIG. 1, the following firstly describes an example of a plasma treatment apparatus in which a semiconductor device manufacturing method of the present invention is carried out. The plasma treatment apparatus 1 shown in FIG. 1 comprises, for example, a process room (process chamber) 11, or a vacuum chamber having an enclosed space therein, a mount table 2 disposed in the center of the bottom of the process room 11 and an upper electrode 3 disposed over the mount table 2 so as to face the mount table 2.

The process room 11 is electrically grounded. In addition, via an exhaust pipe 14 connected with an exhaust port 12 of the bottom, the process room 11 communicates with an evacuator 13. This evacuator 13 is connected with a pressure regulator not shown in the figure. This pressure regulator is configured so as to keep the inside of the process room 11 at a desired degree of vacuum by evacuating the process room 11 according to a signal from a control section 10A described later. A wall of the process room 11 is provided with a wafer W transport gate 15 which can be opened and closed by a gate valve 16.

The mount table 2 comprises a lower electrode 21 and a support block 22 to support the lower electrode 21 from below and is disposed on the bottom of the process room 11 via an insulating member 23. An electrostatic chuck 24 is provided on the top of the mount table 2. A wafer W is mounted on the mount table 2 via this electrostatic chuck 24. The electrostatic chuck 24 is made of dielectric material and contains an electrode foil 26 which is connected to a high voltage dc power supply 25. When voltage is applied to this electrode foil 26 from the high voltage dc power supply 25, static electricity is generated on the surface of the electrostatic chuck 24 and the mounted wafer W on the mount table 2 is electrostatically fixed to the electrostatic chuck 24. The electrostatic chuck 24 has through holes 24 a formed therein to release a back side gas upward from the electrostatic chuck 24 as described later.

The mount table 2 has a coolant flow passage 27 formed therein to flow a coolant (for example, such a widely known conventional one as fluorinated liquid, water or the like). A coolant flowing through this coolant flow passage 27 cools the mount table 2 so that the wafer W mounted on the mount table 2 is cooled down to a desired temperature via the mount table 2. In addition, a temperature sensor not shown in the figure is attached to the lower electrode 21. By this temperature sensor, the temperature of the wafer W on the lower electrode 21 is continuously monitored.

In addition, the mount table 2 has a gas passage 28 formed therein to supply a heat transfer gas such as He (helium) gas as the backside gas. This gas passage 28 is opened in plural places at the top of the mount table 2. These openings communicate with the through holes 24 a so that the backside gas supplied into the gas passage 28 is released upward from the electrostatic chuck 24 via the through holes 24 a. This backside gas diffuses uniformly throughout the space between the electrostatic chuck 24 and the wafer W mounted on the electrostatic chuck 24, which enhances the heat transfer in this space.

The lower electrode 21 is grounded via a high pass filter (HPF) 2 a. A high frequency power supply 21 a of, for example, 13.56 MHz is also connected to the lower electrode 21 via a matcher 21 b. In addition, the lower electrode 21 is circumferentially provided with a focus ring 29 to surround the electrostatic chuck 24 so that generated plasma is focused to the wafer W on the mount table 2 via the focus ring 29.

The upper electrode 3 is a hollow gas shower head having many holes 31 formed uniformly through the bottom surface thereof in order to disperse/supply the process gas into the process room 11. The upper electrode 3 has a gas inlet pipe 32 extended from the central part of the upper surface. This gas inlet pipe 32 passes through the central upper wall of the process room 11 via an insulating member 17. The upstream side of this gas inlet pipe 32 branches into, for example, five branch pipes 32A-32E which are respectively connected with gas supply sources 35A-35E via valves 33A-33E and flow control sections 34A-34E. These valves 33A-33E and flow control sections 34A-34E constitute a gas supply system 36 which can adjust and stop each gas flow from the gas supply sources 35A-35E according to a control signal from the control section 10A as described later. In this example, the gas supply sources 35A, 35B, 35C, 35D, and 35E supply CF₄ gas, C₄F₈ gas, N₂ gas, H₂ gas, and CO₂ gas, respectively.

The upper electrode 3 is grounded via a low pass filter (LPF) 37. To this upper electrode 3, a higher frequency power supply 3 a of, for example, 60 MHz is also connected via a matcher 3 b. The high frequency from the high frequency power supply 3 a connected with the upper electrode 3 is to excite the process gas to the state of plasma whereas the high frequency from the high frequency power supply 21 a connected with the lower electrode 21 is to attract ions from the plasma to the surface of the wafer W by applying the bias voltage to the wafer W. Note that the high frequency power supplies 3 a and 21 a are respectively connected with the control section 10A and, according to control signals therefrom, the powers to be supplied to the upper electrode 3 and the lower electrode 21 are controlled.

For example, the control section 10A of this plasma treatment apparatus 1 is a computer and includes a data processor comprising a program, memory, and CPU. Instructions are incorporated in the program so that the control section 10A sends control signals to individual sections of the plasma treatment apparatus 1 sequentially on an each step-basis in order to give plasma treatment to the wafer W. In addition, the memory may have a region where pressure, time, gas flow, power, and other process parameter values are written. In this case, each time an instruction of the program is executed, the CPU reads some of these process parameters and sends control signals depending on their parameter values to individual sections of the plasma treatment apparatus 1. This program is stored in a computer-oriented storage medium 10B such as a flexible disk, compact disk or MO (magneto-optic disk) and installed in the control section 10A from the storage medium 10B (includes programs on input operations and display for process parameters).

With reference to FIG. 2( a), the following describes film structures formed on the surface of a semiconductor wafer (hereinafter called a wafer) W before this wafer or substrate is processed in the plasma treatment apparatus 1. On the wafer W, an insulating SiO₂ film 41 is deposited by using TEOS (Tetraethoxysilane) as the film-forming material. On this SiO₂ film 41, for example, an organic film 42 is deposited to a thickness of 200 nm. The organic film 42 is composed mainly of carbon. Its carbon content is, for example, 80% by mass at least.

On the organic film 42, a SiO₂ film 43 with a thickness of, for example, 70 nm is formed by the SOG (Spin On Glass) method. On the SiO₂ film 43, a photoresist (PR) film 44 is formed with a thickness of, for example, 150 nm. In this example, a three-layer resist 4 is formed by depositing the organic film 42, the SiO₂ film 43, and the photoresist film 44. The organic film 42 constitutes the lowest layer of the three-layer resist 4.

After exposed to an ArF light source, the photoresist film 44 is developed into a resist pattern 45 whose line width (CD) indicated by L1 in the figure is, for example, 65 nm. At the bottom of the resist pattern 45, the SiO₂ film 43 is exposed. The SiO₂ film 43 not only functions as a hard mask but also functions to make the organic film 42 etching width narrower than CD of the resist pattern 45 since each aperture of the mask pattern 46 formed by etching the SiO₂ film 43 through the resist pattern narrows with depth as described later.

The following describes how a semiconductor device manufacturing method of the present invention is implemented using the plasma treatment apparatus 1. Firstly, the gate valve 16 is opened and the 300 nm (12 inch) wafer W provided with the above-mentioned film structure is carried into the process room 11 by a transport mechanism not shown in the figure. Then, this wafer W is horizontally set on the mount table 2 and electrostatically fixed to the mount table 2. Then, after the transport mechanism is withdrawn from the process room 11, the gate valve 16 is closed. Then, the backside gas is supplied from the gas passage 28 to control the temperature of the wafer W so that its highest part, middle part and lowest part are kept at certain temperatures, for example, 60, 60, and 20 degrees C., respectively. Then, the following steps may be performed.

(Step 1: Etching the SiO₂ Film 43)

While the process room 11 is evacuated by the evacuator 13 via the exhaust pipe 14, CF₄ gas and C₄F₈ gas are supplied at, for example, 200 sccm and 5 sccm respectively from the gas supply system 36 to the surface of the wafer W via the upper electrode 3. The inside of the process room 11 is kept at a certain vacuum, for example, 20 Pa (150 mTorr). Then, a high frequency voltage of 60 MHz for plasma generation is applied at, for example, 500 W to the upper electrode 3 from the high frequency power supply 3 a via the matcher 21 b to excite the CF₄ gas and C₄F₈ gas to the plasma state. Concurrently, a high frequency bias voltage of 13.56 MHz is applied at, for example, 400 W to the lower electrode 51 from the high frequency power supply 21 a via the matcher 21 b.

The SiO₂ film 43 is etched through the resist pattern 45 of the photoresist film 44 as a mask by active carbon (C)/fluorine (F) compound species contained in the plasma SiO₂ film 43. This forms a mask pattern 46 developed in the depth direction and etches the surface of the photoresist film 44. Since the active species are not apt to etch the SiO₂ in lateral directions, the apertures of the mask pattern 46 narrow with depth. When the organic film 42 is exposed at the bottom of the mask pattern 46 as shown in FIG. 2( b), the etching is terminated by stopping high frequency power supply from the high frequency power supplies 21 a and 3 a and gas supply from the gas supply system 36.

(Step 2: Etching the Organic Film 42)

Then, after the remaining CF₄ gas and C₄F₈ gas are removed by evacuating the process room 11 at a certain rate by the evacuator 13, CO₂ gas, H₂ gas, and N₂ gas are supplied at, for example, 200 sccm, 200 sccm, and 200 sccm respectively from the gas supply system 36 into the process room 11 via the upper electrode 3 while the evacuation rate is controlled to a certain rate. The inside of the process room 11 is kept at a certain vacuum, for example, 2.0 Pa (15 mTorr). Then, a high frequency voltage of 60 MHz for plasma generation is applied at 700 W to the upper electrode 3 from the high frequency power supply 3 a via the matcher 21 b to excite the CO₂ gas, H₂ gas, and N₂ gas to the plasma state. Concurrently, a high frequency bias voltage of 13.56 MHz is applied at, for example, 400 W to the lower electrode 21 from the high frequency power supply 21 a via the matcher 21 b.

Carbon dioxide ions (CO₂ ⁺) included in the plasma react with the organic material of the photoresist film 44 and the organic film 42 according to formula (I) below but are not apt to react with SiO₂. Therefore, the generated plasma etches off the photoresist film 44 and etches the organic film 42 through the mask pattern 46 of the SiO₂ film as a mask, resulting in a mask pattern 47 formed.

CO₂ ⁺+C→2CO  (1)

The mask pattern 47 extends in the depth direction and leaves high perpendicularity sidewalls 48. The reason for the high perpendicularity of the sidewalls 48 is as follows. Carbon ions 51 and carbon radicals 52 generated from the carbon dioxide gas and hydrogen ions 53 and hydrogen radicals 54 generated from the hydrogen gas combine to generate CH-based polymer components 55 (FIG. 3( a)). While the mask pattern 47 is formed downward, these polymer components 55 stick to the surface of the sidewall 48 and forms a protect film 56 thereon (FIG. 3( b)). Then, this protect film 56 suppresses the lateral etching of the sidewall 48 by O radicals 57 a and oxygen ions 57 b which are generated from the carbon dioxide gas (FIG. 3( c)).

When the SiO₂ film 41 is exposed at the bottom of the mask pattern 47 as shown in FIG. 4( c), the etching is terminated by stopping high frequency power supply from the high frequency power supplies 21 a and 3 a and gas supply from the gas supply system 36. Then, the SiO₂ film 41 may be etched via the mask pattern 47 on a certain etching condition to form recesses therein. An interconnection metal, for example, copper is buried in these recesses.

According to the above-mentioned embodiment, the mask pattern 47 used to etch the SiO₂ film 41 below the organic film 42 is formed by etching the organic film 42 with plasma containing a mixed gas of CO₂ and H₂ through the mask pattern 46 formed from the SiO₂ film 43 through the resist pattern 45. Due to this manner, the mask pattern 47 is formed so as to have high perpendicularity sidewalls 48 as apparent from the result of an experiment described later. Thus, it is possible to suppress the widening of recesses formed in the SiO₂ film 41 when the SiO₂ film 41 is etched by using the mask patterns 46 and 47. It is therefore possible to bury narrower interconnect lines therein. In addition, as apparent from the result of the experiment described later, it is possible to prevent the mask patterns 46 and 47 from having what is called corner rounding. If corner rounding occurs, each opening becomes remarkably wider at the top as compared with its width at the lowest or middle height. Suppressing such corner rounding is preferable since leak current between laterally spaced interconnect lines is lowered.

In addition, the three-layer resist 4 in the above-mentioned embodiment has the SiO₂ film 43 formed as an intermediate layer between the resist film 44 and the organic film 42. The mask pattern 46 formed from this SiO₂ film 43 is such that each aperture narrows with depth. Since the organic film 42 is etched via this mask pattern 46, it is possible to further suppress the widening of each aperture in the mask pattern 47.

The multi-layered resist is not necessary to be of the three-layer structure. It is also possible to use a four-layer structure as shown in FIG. 4( a). This four-layer resist 6 may have an antireflection organic film 61 formed between the SiO₂ film 43 and the resist film 44. The following describes the process of etching this four-layer resist 6. Firstly, like step 1 in the above-mentioned embodiment, the antireflection film 61 and the SiO₂ film 43 are successively etched through the resist pattern 45 of the photoresist 44 as a mask by using plasma generated from CF₄ and other gases. These films 61 and 43 are formed into such a mask pattern 62 (FIG. 4( b)) that each aperture narrows with depth in the same manner as the mask pattern 46. Then, like step 2 in the above-mentioned embodiment, the organic film 42 is etched via the mask pattern 62 to form a mask pattern 47. Thus, use of such a four-layer resist 6 also attains the same effect as by the above-mentioned embodiment.

As well, the multi-layered resist may be of the two-layer structure as shown in FIG. 5( a). This two-layer resist 60 comprises an organic film 42 and a photoresist film 65 stacked thereon. A resist pattern 45, formed from the photoresist film 65, serves as a mask when the organic film 42 is etched. In addition, the photoresist film 65 contains a greater amount of Si (silicon) than the photoresist film 44 in order to prevent the organic film 42 from being etched off excessively. This two-layer resist 60 is etched according to the procedure of step 2 in the previously mentioned embodiment. As shown in FIG. 5( b), a mask pattern 47 is formed from the organic film 42 without laterally widening the apertures.

The present invention is also applicable to the etching of a wafer W on which a film structure is formed as shown in FIG. 6( a). The film structure shown in FIG. 6( a) is designed to have dual-damascene multi-level interconnection in which not only forming the upper interconnect layer by burying metal in trenches for the upper interconnect layer but also forming via holes for connection between the lower interconnect layer and the upper interconnect layer are performed at the same time. Reference numeral 71 in the figure refers to the lower interconnect layer of copper or other metal. 72 refers to a stopper film to prevent the copper interconnect layer 71 from being etched. The stopper film 72 may be a SiC film. 73 in the figure refers to an insulating SiCOH film which is a porous film having a relative dielectric constant of, for example, 2.7 or lower and containing silicon, carbon, oxygen, and hydrogen. 74 is a hard mask made of, for example, SiO₂ film. The SiO₂ film 74 serves as a cap film to protect the porous SiCOH film 73.

75 in the figure refers to an organic film. Its composition may be the same as the organic film 42 mentioned earlier. 76 is a SiO₂ film serving as a hard mask. 77 is a photoresist film from which a resist pattern 78 is formed. In this example, the organic film 75, the SiO₂ film 76, and the photoresist film 77 constitutes a three-layer resist 7. As a sacrificial film, the organic film 75 is buried in recesses 79 which are formed in the porous SiCOH film 73 to bury electrodes therein. The resist pattern 78 is formed on the recesses 79. In this example, the recesses 79 will form the above-mentioned trenches or via holes once metal (for example, copper) is buried therein by a subsequent process.

The following describes how the above-mentioned film structure including the three-layer resist 7 is sequentially etched. Firstly, like step 1 in the previously mentioned embodiment, the SiO₂ film 76 is etched through the resist pattern 78 of the photoresist film 77 as a mask until the organic film 75 is exposed. Consequently, a mask pattern 81 is formed (FIG. 6( b)). Then, like step 2 in the previously mentioned embodiment, the organic film 75 is etched through the mask pattern 81. Consequently, a mask pattern 82 is formed from the organic film 75 and the remaining photoresist film 77 is removed. This etching is stopped when the remaining organic film 75 buried in the recesses 79 is reduced to a certain height (FIG. 6( c)) after the SiO₂ film 74 is exposed at the bottom of the mask pattern 82.

Then, CF₄ and other process gases are supplied to the process room 11. With these process gases excited to the plasma state, etching is performed by using the organic film 75 as a mask after the SiO₂ film 76 is etched off as shown in FIG. 7( a). Due to this etching, the part of the SiO₂ film 74 exposed to the mask pattern 82 is removed and then the part of the porous SiCOH film 83 exposed to the mask pattern 82 is thinned to a certain thickness.

Then, N₂ gas, CO₂ gas, and H₂ gas are supplied to the process room 11. Like the previously mentioned step 2, the organic film 75 on the SiO₂ film 74 and the organic film 75 buried in the recess 79 are removed as shown in FIG. 7( b) by using their mixed gas excited to the plasma state. Then, CF₄ and other process gases are supplied to the process room 11. With these process gases excited to the plasma state, the part of the SiC film 72 exposed in the recess 79 is etched to expose the lower interconnect layer 71 as shown in FIG. 7( c).

Copper or other metal is buried in the recess 83 formed as described above. Due to this manner, both the upper interconnect layer 84 and electrodes 85 to connect this interconnect layer 84 and the lower interconnect layer 71 are formed at the same time as shown in FIG. 7( d). In this embodiment, a mask pattern with high perpendicularity sidewalls is also fabricated from the organic film 75. This is preferable since it is possible to suppress, for example, the widening of interconnect lines in the upper interconnect layer 84. In addition, since CO₂/H₂ mixed gas plasma is used to etch the organic film 75 buried in the recess 79, it is possible to suppress the damage given to the SiCOH film 73 as compared with O₂ gas plasma-used etching.

In FIG. 8, a process to fabricate another mask pattern is shown. Similar to the wafer W in FIG. 2( a), the wafer W used in this process has a three-layer resist 4 formed thereon as shown in FIG. 8( a). Firstly, according to steps 1 and 2 in the previously mentioned embodiment, a mask pattern 46 is formed from a SiO₂ film 43 and a mask pattern 47 is formed from an organic film 42 via the mask pattern 46 (FIG. 8( b)). Then, with CF₄ gas and C₄F₈ gas in the plasma state as in step 1, the SiO₂ film 43 is removed and the SiO₂ film 41 is etched in the depth direction according to the mask pattern 47. In this manner, a pattern 91 is formed from the SiO₂ film 41 (FIG. 8( c)). Then, with a mixed gas containing CO₂, H₂, and N₂ in the plasma state as in step 2, the organic film 42 is removed (FIG. 8( d)).

Then, an organic film 42 is formed by applying the material so as to fill the pattern 91 with the material. Then, material for the SiO₂ film 43 and material for a photoresist film 44 are applied in this order to the wafer W. A three-layer resist 40 is obtained by forming a resist pattern 45 (FIG. 8( e)). The three-layer resist 40 is the same as the three-layer resist 4 except that its resist pattern 45 does not accord with the pattern 91. Then, steps 1 and 2 are performed again successively. After mask patterns 46 and 47 are formed by etching the SiO₂ film 43 and organic film 42 (FIG. 8( f)), the SiO₂ film 43 is removed and the SiO₂ film 41 is etched in the depth direction according to the mask pattern 47 as in step 1. In this manner, a pattern 92 is formed from the SiO₂ film 41 (FIG. 8( g)). Then, as in step 2, the organic film 42 is removed (FIG. 8( h)).

In the above-mentioned method, after a multi-layered resist is used for etching, another multi-layered resist is formed for another etching. Each multi-layered resist includes an organic film and an intermediate layer. The intermediate layer is provided to control the size of each aperture to be formed in the organic film when etched into a mask pattern. This prevents apertures of the mask pattern from mutually communicating due to lateral etching. Therefore, this is especially effective when a fine pattern is formed below the organic film. By applying the present invention, it is possible to more surely prevent communication between adjacent apertures since a mask pattern with high perpendicularity sidewalls is formed from the organic film.

EXAMPLES Example 1

A wafer W having a SiO₂ film 41 formed thereon and a three-layer resist 4 laminated on the SiO₂ film 41 as shown in FIG. 2, where the previously mentioned embodiment is illustrated, was etched according to the previously mentioned procedure to form a mask pattern 47 from an organic film 42. The vertical section of the mask pattern 47 was photographed around the center and near an edge of the wafer W. The respective films which constitute the three-layer resist 4 on the processed wafer W are the same in thickness as those in the previously mentioned embodiment. As well, the resist pattern 45 is the same in dimension as that in the previously mentioned embodiment. Etching with generated plasma was performed for 60 seconds in step 1 and 52 seconds in step 2 in the previously mentioned procedure. The other conditions were the same as in the previously mentioned embodiment.

FIGS. 9( a) and 9(b) schematically depict the result of imaging around the center and near an edge of the etched wafer W, respectively. The line width in the pattern 101 of the organic film shown in FIG. 9( a) is 70 nm at the top, 72 nm at the bottom, and 75 nm at the middle height. The line width in the pattern 102 of the organic film shown in FIG. 9( b) is 72 nm at the top, 77 nm at the bottom, and 78 nm at the middle height. As apparent from FIGS. 9( a) and 9(b), sidewalls of the patterns 101 and 102 are highly perpendicular and the line widths are uniform regardless of the height. Although it is possible that each aperture widens laterally at the middle height like a bow and corner rounding occurs as described in [Background Art] and [Best Mode for Carrying out the Invention], such bowing and rounding were suppressed.

Comparison Example 1

A wafer W was processed as comparison example 1. After step 1 was performed in the same manner as the above-mentioned example, only CO₂ gas, instead of a mixed gas composed of CO₂, H₂, and N₂, was supplied to the wafer W in step 2. The wafer W was etched with this CO₂ gas in the plasma state. In step 2, except for setting the etching time set to 43 seconds, the process conditions were the same as step 2 for example 1.

FIGS. 9( c) and 9(d) schematically depict the result of photographing around the center and near an edge of the etched wafer W, respectively. The line width in the pattern 103 of the organic film shown in FIG. 9( c) is 71 nm at the top, 78 nm at the bottom, and 85 nm at the middle height. The line width in the pattern 104 of the organic film shown in FIG. 9( d) is 74 nm at the top, 81 nm at the bottom, and 82 nm at the middle height. As apparent from FIGS. 9( c) and 9(d) and these measured line widths, sidewalls of the patterns 103 and 104 have bowing profiles. From this comparison example 1 and example 1, the effect of the present invention was verified. Specifically, by using plasma created by exiting a gas containing CO₂ and H₂, a higher perpendicularity pattern can be formed from the organic film as compared with the use of plasma created from CO₂ gas only.

Comparison Example 2

Wafers W were processed as comparison example 2. After step 1 was performed in the same manner as the above-mentioned example 1, only H₂ gas and N₂ gas, instead of a mixed gas composed of CO₂, H₂, and N₂, were supplied to a wafer W and excited to the plasma state for etching in step 2. The etching time in step 2 was changed for each wafer W. After etching was complete, the vertical section of each wafer W was examined to determine the etching time required to reach the same depth as in the patterns 101 and 102. Except for the supplied gas and etching time, the etching conditions were the same as for step 2 in example 1.

According to the result of the above experiment, a wafer W which was etched for 144 seconds showed the same depth as in the patterns 101 and 102 of example 1. Using a gas which contains H₂ without CO₂ lead to extending the etching time. This may be because H+ ions and others generated as the result of exciting H₂ gas to the plasma state are low in mass and their etching action on the wafer W is small. As apparent from the result of this experiment, it is preferable to supply a process gas containing H₂ and CO₂, rather than a process gas containing H₂ without CO₂, and excite the process gas to the plasma state for etching since it is possible to shorten the etching time and raise the throughput if CO₂ is contained. FIGS. 9( e) and 9(f) schematically depict the result of photographing around the center and near an edge of the 144 second-etched wafer W, respectively. The line width in the pattern 105 of the organic film shown in FIG. 9( e) is 55 nm at the top, 54 nm at the bottom, and 58 nm at the middle height. The line width in the pattern 106 of the organic film shown in FIG. 9( f) is 55 nm at the top, 49 nm at the bottom, and 54 nm at the middle height. In the figure, the patterns 105 and 106 show remarkable corner rounding. Example 1 is preferable also in view of the pattern shape.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 A vertical sectional view showing an example of a plasma treatment apparatus in which a semiconductor device manufacturing method of the present invention is carried out.

FIG. 2 Process diagrams showing how a wafer provided with a three-layer resist is etched by using the semiconductor device manufacturing method of the present invention.

FIG. 3 Diagrams for explaining how sidewalls of an organic film included in the three-layer resist is protected.

FIG. 4 Process diagrams showing a four-layer resist is etched by using the semiconductor device manufacturing method of the present invention.

FIG. 5 Process diagrams showing a two-layer resist is etched by using the semiconductor device manufacturing method of the present invention.

FIG. 6 Process diagrams showing how a wafer W provided with a different three-layer-resist is etched.

FIG. 7 Process diagrams showing how a wafer provided with a different three-layer resist is etched.

FIG. 8 Process diagrams showing how a pattern is formed by repeating a photolithography and an etching process of the present invention.

FIG. 9 Schematic views showing vertical sections of patterns formed in a typical example and comparison examples.

REFERENCE CHARACTERS

-   W semiconductor wafer -   4 three-layered resist -   41 SiO₂ film -   42 organic film -   43 SiO₂ film -   44 photoresist film -   45 resist pattern -   46, 47 mask pattern 

1. A semiconductor device manufacturing method comprising a step of etching an organic film in a multi-layered resist laminated on an etching target film on a substrate, the multi-layered resist including the organic film and a resist film having a resist pattern laminated on the organic film, by a plasma, which has been obtained by making a process gas containing carbon dioxide and hydrogen, along the resist pattern, so as to form a mask pattern for etching the etching target film.
 2. The semiconductor device manufacturing method according to claim 1, wherein the organic film is embedded in a low dielectric constant film formed on the substrate, the low dielectric constant film containing silicon, carbon, oxygen, and hydrogen.
 3. The semiconductor device manufacturing method according to claim 2, wherein the organic film is a sacrificial film.
 4. The semiconductor device manufacturing method according to claim 3 wherein the recess of the low dielectric constant film becomes a via hole where an electrode is buried to connect an upper interconnect layer and a lower interconnect layer in a multi-layered interconnection structure.
 5. The semiconductor device manufacturing method according to one of claims 1 to 4, wherein the organic film contains carbon as a main component.
 6. A storage medium storing a computer program executable by a computer, the program being used in a plasma processing apparatus for etching a substrate, wherein the computer program incorporates steps for performing the semiconductor manufacturing method according to one of claims 1 to
 5. 